GMT+7  -  19.11.2017 - 17:39:10
Records  :  Simpati = 16,  Dosen Lokal = 771,  Berita = 82,  Kerja Sama = 43,  Majalah = 10,  Artikel = 104,  Link = 4,  Buku tamu =
BUKUTAMU Read Sign

We apologize to have not any information right now.
 

CONTENT
   -   Beranda Situs
   -   Agenda LPPM
   -   Buku Tamu
   -   Kerja Sama
   -   SIMPATI

LINKS
   - Universitas Jenderal Achmad Yani
   - Dirjen Pendidikan Tinggi
   - Simlit LPPM Unjani
   - simlitabmas.ris tekdikti.go.id

DOWNLOAD
- Publikasi e-journal Portal Garuda4 Mei 2012.pdf
- REVIEWER DAN PENELITI PAPARAN HASIL LIT.pdf
- RALAT LAMPIRAN JADWAL PAPARAN LIT.pdf
- Agenda Penelitian Tahun 2013 23 Jan 2013.pdf
- PEDOMAN PENELITIAN-Revisi 2013.pdf
- Pemenang Hibah Dana Desentralisasi TA 2013.zip.pdf
- Pedoman Penelitian 2014 LPPM.pdf
- Penerima Hibah DIKTI Tahun 2014.pdf
- Penerimaan proposal penelitian 2014.pdf
- Pengumpulan Abstrak hasil penelitian 2013 untuk SENIJA.pdf
- Pedoman Penelitian Kompetitif Unjani 2015.pdf

MAJALAH Search this web :  

Tahun : 2004 / Volume : 12 / Bulan : May / Nomor : 1
Pengaruh Keausan terhadap Logam Berbasis A1 dan Fe akibat proses abrasif
Oleh : Gadang Priyotomo  |  Pusat Penelitian Metalurgi LIPI

Failure Identification of abrasive wears at Aluminium and Ferrous base material through abrasive test. This problem is identified through abrasive test with using load variable 100 grams to 500 grams and loss material weight variable.

Abrasive test of ferrous material is carried out with direct load method and method of phase until 3000 gram that produce increasing loss weight 0,023 gram and 0,0403 gram. These tendencies cause susceptibility to higher abrasive wear.

Susceptibility of abrasive wear get to be bigger at metal aluminium base is compared metal ferrous base with looking loss weight material is lower than ferrous material.

Kata Kunci: abrasive wear, abrasive test, ferrous base, aluminium base




Judul Lainnya :
- Reksadana Sebagai Salah Satu Alternatif Investasi yang Menarik
- Reduction Material Handling Cost Dengan Memperbaiki Lay-out Fasilitas Pabrik
- Genealogi Pembangunan: Membongkar Positivisme Wacana Pembangunan di Dunia ketiga
- Analisis Kebutuhan Mahasiswa tentang Bimbingan dan Konseling di Perguruan Tinggi Swasta
- Pengaruh Temperatur Perlakuan Panas (Heat Treatment) Terhadap Kestabilan Fasa-fasa senyawa Antar Logam Titanum, Alumunium, Zirkonium

 
Privasi  |  Kontak  |  Peta Situs  |  Developer Copyright © 2006 - 2017 by UNJANI | All Right Reserved